ASTALOY™ PC/ASA 407
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FnYhrL_ASTALOY-PC-ASA-407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ASA 407 is a specialty modified alloy of ASA and Polycarbonate which is designed for automotive injection moulding applications requiring a exceptional depth of dark colours as well as balance of UV stability, impact toughness, product rigidity, heat resistance and mouldability. Typical applications include exterior automotive coloured grilles, station wagon roof rails and B-pillars. Note: The letters "U" or "W" indicate additional UV stabilisation has been incorporated [ ie: ASTALOY™ PC/ASA 407U ]. UV stabilized version meets: GM, GMW15583P-ASA+PC-T4 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 58.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 400 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 30.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 91.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 97.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 104 | °C | |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 225 to 245 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061R 65308 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Sylvin 2990-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Fluon® LM-ETFE AH-3000 | Asahi Glass Co., Ltd. | ETFE | Fluon® |
| Lion Idemitsu Composites PPS C-140HG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| ALTECH® PC ECO 1000/141 UV IM | ALBIS PLASTIC GmbH | PC | ALTECH® PC |