TECHNYL® C R 218 V30 BLACK 1 N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FnGArr_TECHNYL-C-R-218-V30-BLACK-1-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® CR 218 V30 Black 1N is a polyamide 6, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. It contains recycled raw materials. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.75 | % | |
| Flow | 0.37 | % | |
| Molding Shrinkage Isotropy | 0.490 | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A |
| Flexural Modulus | 8800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 208 | °C | ISO 75-2/Af |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.60 mm | 650 | °C | |
| 3.20 mm | 650 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silmar® SIL94BA-1575 | Interplastic Corporation | Polyester, TS | Silmar® |
| DAPCO™ 3100FR | Cytec Industries Inc. | Epoxy | DAPCO™ |
| DOMAMID® 66G25V0P 1003 A | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Ensinger TECAPET® | Ensinger Inc. | PET | Ensinger |
| Sylvin 8999-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |