Duron PEI 1110-WHT
| Category: | PEI , Polyether Imide |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | Duron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FmnmaS_Duron-PEI-1110-WHT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duron PEI 1110-WHT is a white pigmented polyetherimide that offers a superior combination of mechanical, electrical, and thermal properties. PEI is inherently flame resistant with low smoke emission. It provides outstanding processability and good chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.50 - 0.80 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.60 - 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 105 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 10 | % | ASTM D638 |
| Fracture, 23°C | 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 160 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 199 | °C | ASTM D648 |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256, 23°C: 6 kJ/m²Unnotched Izod Impact, ASTM D256, 23°C: 140 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safrene® M 5010PE100 BLK | Safripol (PTY) LTD | HDPE | Safrene® |
| 3M™ Dyneon™ PTFE Compound TF 7149 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| APEX® RE 8118 | Teknor Apex Company | PVC, Rigid | APEX® |
| LNP™ LUBRICOMP™ JX91198 compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ RX98372H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |