LARIPUR® LPR 5020
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | COIM S.p.A. |
| Trademark: | LARIPUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FmUQap_LARIPUR-LPR-5020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LARIPUR®LPR 5020 is a thermoplastic polyurethane elastomer (polyester)(TPU-polyester) material,. This product is available in North America, Latin America or Europe. The processing method is injection molding. LARIPUR®The main features of LPR 5020 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 75.0 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% strain | 8.20 | MPa | ASTM D412 |
| 100% strain | 10.6 | MPa | ASTM D412 |
| 300% strain | 26.8 | MPa | ASTM D412 |
| Tensile Strength (Break) | 58.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 470 | % | ASTM D412 |
| Tear Strength | 132 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 70 hr | 24 | % | ASTM D395 |
| 70°C, 22 hr | 50 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Additional Information |
|---|
| Abrasion loss, DIN 53516: 35 mm³Tosion Test, ASTM D 1043, 20° C: 20 MPaTosion Test, ASTM D 1043, -20° C: 190 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Technother® A-SV15-T | Poly Plastic | PBT | Technother® |
| T-Blend® 5792N-PE | TSRC Corporation | TPE | T-Blend® |
| VORAZ™ 511 | Greene, Tweed & Co. | Perfluoroelastomer | VORAZ™ |
| Globalprene® 3741 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| LNP™ THERMOCOMP™ OF008A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ THERMOCOMP™ |