VECTRA® E531i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Flsu9W_VECTRA-E531i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mineral filled grade with low warp, easy flow and smooth surface appearance. Chemical abbreviation according to ISO 1043-1:LCP Inherently flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 325 - 335 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 335 - 345 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 335 to 345°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2261 | RTP Company | PEEK | RTP |
| Sekisui PVC HA-27F | Sekisui (Hong Kong) Limited | PVC, Unspecified | Sekisui PVC |
| Toughblend® PA66-1900 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| NYLOY® UB-0010N C45N2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| ELASTOSIL® R plus 573/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |