VENELENE® FA-0240

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Poliolefinas Internacionales, C.A. (Polinter)
Trademark:	VENELENE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Flgqgr_VENELENE-FA-0240.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features:

Excellent processability, transparency and shines.

Applications:

Automatic Packaging Film of 30-50 µm thickness.

Heavy duty bags (<10 Kg).

Supermarket and boutique bags.

General Information
Additive	Anti-caking agent Antioxidation slip agent
Features	Low density smoothness Anti-caking property Antioxidation Workability, good Definition, high Excellent appearance
Uses	Packaging Films Bags Heavy packing bag
Forms	Particle
Processing Method	Film extrusion Blow molding Extrusion Extrusion blow molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.920	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.9	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Film Puncture Force (50 µm)	10.3	N
Tensile Strength			ASTM D882
MD : Break, 50 µm	24.0	MPa	ASTM D882
TD : Break, 50 µm	15.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 50 µm	150	%	ASTM D882
TD : Break, 50 µm	500	%	ASTM D882
Elmendorf Tear Strength			ASTM D1922
MD : 50 µm	400	g	ASTM D1922
TD : 50 µm	150	g	ASTM D1922
Impact Resistance, Film	280	J/cm	ASTM D1709
Toughness, Film			ASTM D882
MD	30.0	MPa	ASTM D882
TD	54.0	MPa	ASTM D882

Optical	Nominal Value	Unit	Test Method
Transmittance (50.0 µm)	80.0	%	ASTM D1003
Haze (50.0 µm)	13	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	120 - 180	°C

Extrusion instructions
Blow up ratio (BUR): 2 - 3. Die gap: 0.7 -1.0 mm. Frost line Height: 4 -5 times die gap Diameter.

Resin Grade	Manufacturer	Category	Trademark
RTP 685 FR HEC	RTP Company	ABS	RTP
TAROLOX 111 G5 DX03	Taro Plast S.p.A.	PET	TAROLOX
TOTAL Polypropylene PPH 3866	TOTAL Refining & Chemicals	PP Homopolymer	TOTAL Polypropylene
LUVOCOM® 20-0664	Lehmann & Voss & Co.	PPA	LUVOCOM®
Perlast® G74P	Precision Polymer Engineering Ltd.	Perfluoroelastomer	Perlast®