Braskem PE SLH118
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FlOnl1_BraskemPESLH118.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 1100 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1400 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 200 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm | 210 | MPa | ASTM D790 |
| Dart Drop Impact 1 | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 300 | g | ASTM D1922 |
| TD : 38 µm | 510 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 84 | % | ASTM D6866 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SORVEX 400 | Sorensen Ventures | PBT | SORVEX |
| Toyolac® 100G-20 | Toray Resin Company | ABS | Toyolac® |
| Viprene™ G45A-32U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| NEFTEKHIM PP 1522J | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Karina YELLOW PVC COMPOUND 752D02/101-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |