LNP™ LUBRILOY™ D2000 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FkkDxn_LNP-LUBRILOY-D2000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing a Proprietary Non-Halogenated Lubrication System. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRILOY* Compound D Product reorder name: D2000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.81 | % | ISO 294-4 |
| Flow : 24 hr | 0.84 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2050 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/5 |
| Break 3 | 46.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.1 | % | ASTM D638 |
| Yield | 6.6 | % | ISO 527-2/5 |
| Break 5 | 47 | % | ASTM D638 |
| Break | 170 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2170 | MPa | ASTM D790 |
| -- 7 | 1970 | MPa | ISO 178 |
| Flexural Stress | 77.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.31 | ||
| vs. Itself - Static | 0.22 | ||
| Wear Factor - Washer | 38.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D256 |
| 23°C 8 | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 50.0 | J | ASTM D3763 |
| -- | 42.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 128 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.6E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 304 to 316 | °C | |
| Processing (Melt) Temp | 304 to 316 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 B 1000/270 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Corton® 1009 HS NATURAL | PolyPacific Pty. Ltd. | PP, Unspecified | Corton® |
| Geon™ Vinyl Flexible R4294W | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hifax RTA3263EUV | LyondellBasell Industries | TPO (POE) | Hifax |
| HOPELEN Y-130 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |