Novalloy-S S3100
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FkZQWd_NovalloySS3100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-S S3100 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in the Asia-Pacific region,. The main characteristics of Novalloy-S S3100 are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 109 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 99.0 | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.50 mm) | 35 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 85.0 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 3 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 400 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 150 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 127 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 42 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 220 - 250 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 5.00 - 20.0 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Crystal rePS-5 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| DI-COAT E-4669 | Hapco Inc. | TP, Unspecified | DI-COAT |
| LARIPUR® LPR 107-93A | COIM S.p.A. | TPU-Capro | LARIPUR® |
| Karina RED PVC COMPOUND 902-42/291-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF00C compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |