SCHULABLEND® (ABS/PA) M/MK 6101 GF8 U
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + PA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FiVtDy_SCHULABLENDABSPAMMK6101GF8U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 8% glass fiber reinforced ABS/PA6 blend with high impact strength, high flow, UV-stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 5.00 | cm³/10min | ISO 1133 |
| 260°C/5.0 kg | 9.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 109 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 45.0 | MPa | ISO 527-2/1/5 |
| Tensile Strain (Break) | 9.0 | % | ISO 527-2/1/5 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 6.0% strain | 78.0 | MPa | ISO 178 |
| 3.5% strain | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 48 | kJ/m² | ISO 179/1eU |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPSiV™ 3451-80A NAT | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Elvaloy® 4924 | DuPont Packaging & Industrial Polymers | TP, Unspecified | Elvaloy® |
| LNP™ THERMOCOMP™ GF004 compound | SABIC Innovative Plastics | PSU | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ 5E003M compound | SABIC Innovative Plastics | PVDF | LNP™ THERMOCOMP™ |
| SEQUEL® 1580-UV 598F ANTHRACITE | LyondellBasell Industries | TPO (POE) | SEQUEL® |