Lumiplas庐 LD590T
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumiplas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FhRQU1_Lumiplas-LD590T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Light diffusion, High Impact Application (LED) Lamp cover, Signboard, Lighting Decoration of Electronic Device |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 110 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 6.40 mm) | 81.0 | °C | ASTM D648 |
| CLTE - Flow | 8.4E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Nozzle Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 200 - 230 | °C | |
| Cylinder Zone 3 Temp. | 210 - 240 | °C | |
| Cylinder Zone 4 Temp. | 220 - 250 | °C | |
| Adapter Temperature | 220 - 250 | °C | |
| Melt Temperature | 230 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| RollStack Temperature: 60 to 100°CRollStack Temperature: 70 to 90°CRollStack Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Malen E FABS 23-D022 | LyondellBasell Industries | LDPE | Malen |
| ADENE GCJB | A.D. Compound spa | PP Homopolymer | ADENE |
| CP PRYME® Nylon 6 N100LZ NAT | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| OTECH TPO OTE6519 - Cord Insulation | OTECH Corporation | TPO | OTECH TPO |
| Starex LX-0981M | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |