Biograde® C 7500
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Biograde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fgoyrg_Biograde-C-7500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Biograde®C 7500 is a biodegradable polymer (Biodeg Polymers) material,. This product is available in Europe, and the processing method is injection molding. Biograde®The main characteristics of C 7500 are: environmental protection/green. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Apparent Density | 0.76 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 17 - 21 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 15.0 - 18.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture | 65.0 | MPa | ISO 527-2 |
| -- | 66.0 | MPa | ISO 527 |
| Tensile Strain (Break) | 13 | % | ISO 527-2 |
| Flexural Modulus | 2950 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 70.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 13 | % | ISO 527 |
| Flexural Strain at Break | No Break | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/A |
| Melting Temperature (DSC) | > 180 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 30.0 - 75.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Feeding Zone: 60°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safrene® C 7260 | Safripol (PTY) LTD | HDPE | Safrene® |
| Sylvin 2905-85 White 1494 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEFTEKHIM PE 6250D (506H4) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Nanjing Hongrui PA66 A306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Delta PPO FR1G41 | Delta Polymers | PPE+PS | Delta |