Witcom PA66 2006/274
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FfrIPG_Witcom-PA66-2006-274.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA66 2006/274 is a polyamide 66 (nylon 66) product that contains fillers. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 - 0.40 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 5.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 165 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus | 14000 | MPa | ISO 178 |
| Flexural Stress | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 8.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | °C | ISO 75-2/A |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 100 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SB891 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| SILVER® EUL105-K/UL1007 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| Diamond ABS 3500 LG | Network Polymers, Inc. | ABS | Diamond ABS |
| HANWHA CLBB-850BK | Hanwha Chemical | LDPE | HANWHA |
| KOPLA ABS KSG1020 | KOPLA Co., Ltd. | ABS | KOPLA ABS |