POCAN® BF 4409 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FfiKSy_POCANBF4409000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 7 % glass fibers, injection molding, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.49 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 250°C, 2.00mm 1 | 1.2 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | % | ISO 2577 |
| Flow direction : 250°C, 2.00mm 3 | 1.3 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.20 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 155 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4200 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 120 | MPa | ISO 178/A |
| 23°C 6 | 130 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.9 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GFHMR, 11-050, GF7; ISO 1043-PBT GF FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (211°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.60 | IEC 60250 | |
| 23°C, 1 MHz | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 2.0E-3 | IEC 60250 | |
| 23°C, 1 MHz | 0.019 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.400 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 725 | °C | IEC 60695-2-13 |
| 1.60 mm | 725 | °C | IEC 60695-2-13 |
| 3.00 mm | 725 | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 31 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND POMC TX90-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Fainplast PVC KL 0993 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| EGYPTENE HD 5218 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| Idemitsu PS SEHI-210 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| POLIMAXX 2563LCXTA5 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |