LNP™ LUBRICOMP™ DP003 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FfCxwv_LNP-LUBRICOMP-DP003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4530 Product reorder name: DP003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.90 to 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.80 to 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2230 | MPa | ASTM D638 |
| -- | 2170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 49.0 | MPa | ASTM D638, ISO 527-2 |
| Break | 42.7 | MPa | ASTM D638 |
| Break | 41.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.6 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2 |
| Break | 35 | % | ASTM D638 |
| Break | 41 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1900 | MPa | ASTM D790 |
| -- | 1840 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 75.2 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.10 | ||
| vs. Itself - Static | 0.26 | ||
| Wear Factor - Washer | 42.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D256 |
| 23°C 2 | 32 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 28.4 | J | ASTM D3763 |
| -- | 61.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 129 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPRO PP RG4 | Rondo Plast AB | PP, Unspecified | REPRO |
| Spartech Polycom SC1-1230 | Spartech Polycom | ABS | Spartech |
| DOMAMID® 66G35V0P 1001 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Eltex® P KS417 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Kingfa API-1025 | Kingfa | PP, Unspecified | Kingfa |