AKROMID® B3 M 40 natural (2795)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FfCfHt_AKROMID-B3-M-40-natural-2795-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 M 40 natural (2795) is a 40 % mineral filled polyamide 6 with very good surface and low warpage. Characteristic applications are chrome-plated handles, housings and switches in the automotive as well as covers in the sanitary industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.45 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.90 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.0 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 6.1 | -- | % | ISO 178 |
| Tensile Modulus | 5500 | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 7.0 | 25 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 5000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 130 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 120 | -- | kJ/m² | |
| 23°C | 110 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GP2201 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Axiall PVC 59996J | Axiall Corporation | PVC, Flexible | Axiall PVC |
| ESENTTIA 40H92N | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| LUVOCOM® 1-9061/T | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 7833-85 Green 3192 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |