MARPOL® Homo 20.NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® Homo |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FeYURo_MARPOL-Homo-20-NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Additives: Nucleation and Antistat Recommended Applications: Caps, closures, and thin wall containers Homo 20.NA complies with all applicable FDA regulations for food contact applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 127 | °C | ASTM D648 |
| Melting Temperature | 166 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D311 GF30 | Polykemi AB | PBT | POLYshine |
| Bayfit® 566 (90 Index, 3.3 pcf) | Covestro - PUR | PUR-Ether/MDI | Bayfit® |
| DESOX™ DSC640M5 | DESCO Co., Ltd. | PBT+PET | DESOX™ |
| FRblend® PS-1302 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PS (GPPS) | FRblend® |
| RTP 699 X 118417 EG | RTP Company | ABS | RTP |