KumhoSunny AES HW600G
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny AES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FeMXTT_KumhoSunny-AES-HW600G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AESHW600G is a kind of AES resin with good weather resistance ability, offering high rigidity ,high toughness and excellent processability. Application:automobile outside parts as side-mirror, radiator grill, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 17 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.70 | % | ASTM D955 |
| -- | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 52.0 | MPa | ASTM D638 |
| -- | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break | 22 | % | ASTM D638 |
| Break | 25 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| -- 1 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 72.0 | MPa | ASTM D790 |
| -- 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 3.20 mm | 200 | J/m | ASTM D256 |
| 23°C 5 | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 6 | 78.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525 7 |
| -- | 96.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 95.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 240 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 4J |
| 5 . | 5.5J |
| 6 . | 120°C/h |
| 7 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 83EK10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| TEKAMID™ TA210SG15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| MTM® 248S | Cytec Industries Inc. | Epoxy | MTM® |
| THERMOLAST® K TC7GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| NEXUS PE LLDPE-2020 Granular | Nexus Resin Group, LLC. | LLDPE | NEXUS PE |