LNP™ STAT-LOY™ A3000 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fe4cZT_LNPSTATLOYA3000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY A3000 is a compound based on Acrylonitrile butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistatic. Also known as: STAT-LOY A Also known as: LNP* STAT-LOY* Compound A Product reorder name: A3000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 1.1 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 2010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 36.0 | MPa | ASTM D638 |
| Fracture | 31.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.1 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Fracture 5 | 6.0 | % | ASTM D638 |
| Fracture | 24 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2090 | MPa | ASTM D790 |
| -- 7 | 1980 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 59.0 | MPa | ISO 178 |
| Fracture, 50.0mm span 8 | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D256 |
| 23°C 9 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 32.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 88.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 91.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 76.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 76.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 9.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 182 - 193 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 204 - 216 | °C | |
| Processing (Melt) Temp | 199 - 210 | °C | |
| Mold Temperature | 10.0 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE 601C | The Dow Chemical Company | LDPE | DOW™ LDPE |
| ALTECH® ABS A 1000/106 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| Delta PPR-2G50 | Delta Polymers | PP Copolymer | Delta |
| LNP™ THERMOCOMP™ YF004 compound | SABIC Innovative Plastics | TPEE | LNP™ THERMOCOMP™ |
| Sylvin 4280-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |