Category: | PP Homopolymer , Polypropylene Homopolymer |
Manufacturer: | Polychim Industrie S.A.S. |
Trademark: | Polychim |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | FcrUw6_PolychimHS15XC.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
APPLICATIONS :
|
General Information | |
---|---|
Additive |
|
Features |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 0.900 | g/cm³ | ASTM D1505 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 70 - 80 | g/10 min | ASTM D1238 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 1(Yield) | 36.0 | MPa | ASTM D638 |
Tensile Elongation 2(Yield) | 9.0 | % | ASTM D638 |
Flexural Modulus - 1% Secant 3 | < 1700 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 26 | J/m | ASTM D256A |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, not annealed | 116 | °C | ASTM D648 |
1.8 MPa, not annealed | 57.0 | °C | ASTM D648 |
Vicat Softening Temperature | |||
-- | 154 | °C | ASTM D1525 4 |
-- | 95.0 | °C | ASTM D1525 5 |
Optical | Nominal Value | Unit | Test Method |
---|---|---|---|
Yellowness Index | < 0.0 | YI | DIN 6167 |
Note Message | |
---|---|
1 . | 50 mm/min |
2 . | 50 mm/min |
3 . | 1.3 mm/min |
4 . | 速率 A (50°C/h), 压 力1 (10N) |
5 . | 速率 A (50°C/h), 载荷2 (50N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
DOMAMID® 66Y10 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
Elvaloy® AC 1218 | DuPont Packaging & Industrial Polymers | EMA | Elvaloy® |
Lucent PC PC/ABS-FR5 | Lucent Polymers, Inc. | PC+ABS | Lucent PC |
Sylvin 9067-90 Orange 566 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
NYLOY® KF-0020N 6231W | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |