Badamid® LA70 GF15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FcQDUo_Badamid-LA70-GF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LA70 GF15 is a Polyamide 66 (Nylon 66) material filled with glass fiber. It is available in Europe. Primary attribute of Badamid® LA70 GF15: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.7 to 7.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 to 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 10 | % | ISO 527-2/5 |
| Flexural Stress (23°C) | 180 | 125 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 8.0 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 43 | -- | kJ/m² | |
| 23°C | 45 | 70 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 5.5 | 6.5 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 260 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 3.0E-5 to 3.5E-5 | -- | cm/cm/°C | |
| Transverse | 7.0E-5 to 8.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | 240 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.16 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® W 2320 003 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Alathon® L5840 | LyondellBasell Industries | HDPE | Alathon® |
| INNOPOL® PP CS 1-3810 | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Sylvin 5132-86 Clear Green 3164 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ SCL36 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |