LTP ZW-3650
| Category: | PPS Alloy , Polyphenylene Sulfide Alloy |
| Manufacturer: | Chengdu Letian Plastics Co., Ltd |
| Trademark: | LTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FbxILZ_LTP-ZW-3650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resin of LTP ZW-3600 serials is crystal whisker reinforced composite materials based on high molecular weight linear PPS and PEEK alloy. With the characteristics of excellent high strength, rigidity, wear-resisting, heat-resisting, chemical-resisting and outstanding mold technology, the materials can meet the needs of product to replace copper alloy and hard alloy for varied fields. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | GB/T 1033 |
| Melt Mass-Flow Rate (MFR) | 15 to 30 | g/10 min | GB/T 3682 |
| Molding Shrinkage 1 | |||
| Across Flow : 3.00 mm | < 0.20 | % | |
| Flow : 3.00 mm | < 0.10 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 to 0.30 | % | GB/T 1034 |
| PV Limit | 2300 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 1 | µm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | > 265 | °C | GB/T 1634 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (A-Scale) | 80 | GB/T 9342 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 125 | MPa | GB/T 1040 |
| Tensile Strain (Break) | 0.60 | % | GB/T 1040 |
| Flexural Stress | 180 | MPa | GB/T 1042 |
| Compressive Stress | 290 | MPa | GB/T 1041 |
| Coefficient of Friction (Dynamic) | 0.020 | GB/T 3960 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | GB/T 1043 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | GB/T 2572 | ||
| Flow | -2.0E-5 | cm/cm/°C | |
| Transverse | -3.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 mm |
| 2 . | 10MPa/24hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL ABS-G10 | Polymer Resources Ltd. | ABS | PRL |
| S&E Wire & Cable GA-1941-AFRO | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Sumikon® PM-9501 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| Fortron® ICE 714A | Celanese Corporation | PPS | Fortron® |
| LNP™ LUBRICOMP™ SFL36 compound | SABIC Innovative Plastics Europe | Nylon 12 | LNP™ LUBRICOMP™ |