| 30% Glass Fiber Reinforced, Chemically Coupled, UV Stabilized, Polypropylene, Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Dart Drop Impact | 0.565 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 142 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 204 - 232 | °C | |
| Middle Temperature | 210 - 238 | °C | |
| Front Temperature | 216 - 243 | °C | |
| Nozzle Temperature | 221 - 232 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - application dependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall thickness dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® R 359 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| BESTPOLUX PCBM/01 | Triesa Plastics | PC+PBT | BESTPOLUX |
| Lupoy® 1201HP-08 | LG Chem Ltd. | PC | Lupoy® |
| PERLER® N09V3000B10 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| Sylvin 3240-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |