MAJORIS G401 - 7841/E
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fbfn9G_MAJORIS-G401---7841-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS G401 - 7841/E is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties. This product is high heat distortion temperature stabilised. MAJORIS G401 - 7841/E is available both in natural (MAJORIS G401) and black (MAJORIS G401 - 8229). Other colours can be provided on request. APPLICATIONS MAJORIS G401 - 7841/E is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS G401 - 7841/E make it suitable for:
MAJORIS G401 - 7841/E can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 119 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus | 7850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 27 | kJ/m² | ISO 179/1eA |
| 23°C | 24 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 52 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 162 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| CLTE - Flow | ASTM D696 | ||
| -30°C | 4.4E-5 | cm/cm/°C | ASTM D696 |
| 23°C | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10%Holding time: as long as practical |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F086-AAA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Edgetek™ AT-1000 | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| KOPLA PA6 KNR1031 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Hylar® 5000 HG | Solvay Specialty Polymers | PVDF | Hylar® |
| Sylvin 8235-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |