Moharamplast HDPE MP6004-100
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Moharamplast S.A.E |
| Trademark: | Moharamplast HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FbS5GG_Moharamplast-HDPE-MP6004-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A black high density polyethylene (HDPE) compound classified as PE100. It contains >2.2% well dispersed carbon black class A1 to ensure outstanding weather resistance, provides high tensile strength with high resistance against fast and slow crack propagation. The added carbon black type is less sensitive to moisture despite the hygroscopic behavior due to its fine particle size. It also shows a very high impact resistance throughout its entire temperature range combined with an acute resistance to fracture which is a significant advantage in applications where temperature is very low so it can be used at temperatures ranging from -50°C to 60°C. Safety MP6004-100 is classified as no-dangerous material. We advise you to follow our safety guidelines and recommendations in our Material Safety Data Sheet. Typical Applications MP6004-100 is manufactured from high density polyethylene (HDPE) resin meeting the requirements of ASTM D3035, it fulfills the requirements of ASTM D2837 for hydrostatic design basis. MP6004-100 is recommended for pipe systems in the applications field of drinking water pressure pipes, mining pipe, industrial pipes, sewage pipes and corrugated pipes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.40 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | > 5000 | hr | ASTM D1693 |
| Carbon Black Content | > 2.2 | % | ASTM D1603 |
| Carbon Black Dispersion | A1 | ISO 18553 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 70 | min | ASTM D3895 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 to 210 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 24.0 | MPa | |
| Break | 28.0 | MPa | |
| Tensile Elongation (Break) | > 700 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 115 | °C | ASTM D1525 |
| Melting Temperature | > 120 | °C | ASTM D2117 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 90.0 | °C | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 190 to 210 | °C | |
| Cylinder Zone 5 Temp. | 190 to 210 | °C | |
| Melt Temperature | 200 to 220 | °C | |
| Die Temperature | 200 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^ F20 FR6 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Thermec™ 6250RMC65 | Technical Polymers, LLC | PPS | Thermec™ |
| Durepol® PBT A3 HL PRTA011 BT315 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Generic PVC, Rigid | Generic | PVC, Rigid | Generic |
| Sylvin 9077-85 Grey 9331 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |