GLAMIDE® NB-5550
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FbLkm8_GLAMIDE-NB-5550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®NB-5550 is a polyamide product that contains 30% mineral fillers. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.27 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.40 - 0.70 | -- | % | ASTM D955 |
| 3.00 mm | 1.2 - 1.6 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.40 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 1.7 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 110 | 100 | MPa | ASTM D638 |
| Yield, 23°C | 66.0 | 55.0 | MPa | ASTM D638 |
| Yield, 80°C | 31.0 | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.8 | -- | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 8000 | 7200 | MPa | ASTM D790 |
| 23°C | 5100 | 3800 | MPa | ASTM D790 |
| 80°C | 3200 | 1500 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 170 | 163 | MPa | ASTM D790 |
| Yield, 23°C | 105 | 85.0 | MPa | ASTM D790 |
| Yield, 80°C | 50.0 | 35.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 38 | 65 | J/m | ASTM D256 |
| 23°C | 50 | 200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 202 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 119 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 30 | 23 | kV/mm | ASTM D149 |
| Arc Resistance | 130 | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 - 290 | °C | |
| Mold Temperature | 50.0 - 120 | °C | |
| Injection Pressure | 50.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 40K | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Styrolution PS 116N/L | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| 3M™ Dyneon™ PTFE TF 2035Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Andur 800 AP/Curene® 442 | Anderson Development Company | PUR-Est/eth,TDI | Andur |
| LNP™ STAT-LOY™ 63000CTC compound | SABIC Innovative Plastics Asia Pacific | PC+Polyester | LNP™ STAT-LOY™ |