Ultramid® 8233G HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FbInzn_Ultramid-8233G-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in non-heat stabilized (Ultramid 8233G) and/or pigmented versions. Applications Ultramid 8233G HS is generally recommended for applications such as power tool housings, weed trimmer components, gears, automotive housings and under hood applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.1 | -- | % | ISO 62 |
| Saturation | 6.4 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.4 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.8 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 10500 | 11600 | MPa | |
| 23°C | 10100 | 5840 | MPa | |
| 80°C | 4430 | 4300 | MPa | |
| 121°C | 3550 | 3400 | MPa | |
| Tensile Strength | ||||
| Break, -40°C | 283 | 255 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 195 | 125 | MPa | ASTM D638 |
| Break, 80°C | 110 | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 121°C | 83.0 | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 185 | 125 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, -40°C | 3.6 | 3.5 | % | ASTM D638 |
| Break, 23°C | 3.5 | 6.0 | % | ASTM D638, ISO 527-2 |
| Break, 80°C | 7.0 | 6.0 | % | ASTM D638 |
| Break, 121°C | 7.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | ||||
| -40°C | 9830 | 10200 | MPa | ASTM D790 |
| 23°C | 9040 | 5130 | MPa | ASTM D790 |
| 65°C | 4020 | -- | MPa | ASTM D790 |
| 90°C | 3750 | -- | MPa | ASTM D790 |
| 121°C | 3320 | -- | MPa | ASTM D790 |
| 23°C | 8200 | 5200 | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 380 | 361 | MPa | ASTM D790 |
| 23°C | 297 | 179 | MPa | ASTM D790 |
| 65°C | 160 | -- | MPa | ASTM D790 |
| 90°C | 140 | -- | MPa | ASTM D790 |
| 121°C | 112 | -- | MPa | ASTM D790 |
| 23°C | 260 | 130 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 88 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| -40°C | 110 | 110 | J/m | ASTM D256 |
| 23°C | 150 | 240 | J/m | ASTM D256 |
| -40°C | 8.5 | -- | kJ/m² | ISO 180 |
| 23°C | 10 | -- | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 4.07 | 6.78 | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 3.8E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 2.1E-5 | -- | cm/cm/°C | |
| Transverse | 7.0E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 44 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 100 Hz | 4.20 | -- | ||
| 1 MHz | 3.60 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.020 | -- | ||
| 1 MHz | 0.020 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.600 mm | HB | -- | ||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 A5G6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 612 | Shandong PA612 |
| BESTNYL SE25VI02A | Triesa Plastics | Nylon 66 | BESTNYL |
| FM® 404NA | Cytec Industries Inc. | Epoxy | FM® |
| PEARLSTICK® 45-40/08 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |
| Hostacom EBS 777D White | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |