Generic PS (HIPS)
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fb63hm_Generic-PS-HIPS-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PS (HIPS) This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 - 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.05 | g/cm³ | ISO 1183 |
| -- | 1.04 | g/cm³ | ASTM D1505 |
| Apparent Density | |||
| -- | 0.60 - 0.70 | g/cm³ | ASTM D1895 |
| -- | 0.60 - 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 2.4 - 10 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 3.0 - 12 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 3.89 - 9.90 | cm³/10min | ISO 1133 |
| Spiral Flow | 43.8 - 57.0 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.45 - 0.61 | % | ASTM D955 |
| 23°C | 0.54 - 0.55 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.036 - 0.11 | % | ASTM D570 |
| 23°C, 24 hr | 0.10 | % | ISO 62 |
| Saturated, 23°C | 0.098 - 0.15 | % | ASTM D570 |
| Saturated, 23°C | 0.088 - 0.11 | % | ISO 62 |
| Equilibrium, 23°C | 0.099 - 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.098 - 0.10 | % | ISO 62 |
| Bound Styrene | 0.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 46 - 113 | ASTM D785 | |
| 23°C | 54 - 101 | ISO 2039-2 | |
| Ball Indentation Hardness | 65.0 - 91.1 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1530 - 2460 | MPa | ASTM D638 |
| 23°C | 1400 - 2230 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 17.1 - 31.2 | MPa | ASTM D638 |
| Yield, 23°C | 16.0 - 32.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 18.3 - 28.3 | MPa | ASTM D638 |
| Fracture, 23°C | 19.7 - 30.8 | MPa | ISO 527-2 |
| 23°C | 19.9 - 31.4 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.4 - 61 | % | ASTM D638 |
| Yield, 23°C | 1.5 - 1.8 | % | ISO 527-2 |
| Fracture, 23°C | 27 - 63 | % | ASTM D638 |
| Fracture, 23°C | 28 - 61 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1330 - 2630 | MPa | ASTM D790 |
| 23°C | 1900 - 2430 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 31.7 - 53.7 | MPa | ASTM D790 |
| 23°C | 31.3 - 51.3 | MPa | ISO 178 |
| Yield, 23°C | 29.4 - 53.7 | MPa | ASTM D790 |
| Fracture, 23°C | 29.0 - 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.8 - 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 4.9 - 120 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 62 - 150 | J/m | ASTM D256 |
| 23°C | 2.0 - 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 53 - 810 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 10.2 - 18.3 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 74.7 - 96.9 | °C | ASTM D648 |
| 0.45 MPa, annealed | 86.9 - 93.9 | °C | ASTM D648 |
| 0.45 MPa, annealed | 84.8 - 89.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.9 - 87.5 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 67.8 - 85.4 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 80.9 - 98.9 | °C | ASTM D648 |
| 1.8 MPa, annealed | 76.6 - 94.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 84.3 - 105 | °C | ASTM D1525 |
| -- | 81.4 - 100 | °C | ISO 306 |
| CLTE - Flow | |||
| -- | 8.9E-5 - 9.1E-5 | cm/cm/°C | ASTM D696 |
| -- | 8.0E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.17 | W/m/K | ISO 8302 |
| RTI Imp | 50.0 - 50.3 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+3 - 1.0E+16 | ohms | ASTM D257 |
| -- | 1.0E+13 - 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 50 - 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 - 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 16 - 160 | kV/mm | ASTM D149 |
| 23°C | 49 - 160 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.50 - 2.60 | ASTM D150 | |
| 23°C | 2.50 | IEC 60250 | |
| Dissipation Factor (23°C) | 3.0E-4 - 4.1E-4 | IEC 60250 | |
| Comparative Tracking Index | 393 - 505 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 14 - 98 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 69.5 - 82.4 | °C | |
| Drying Time | 1.4 - 3.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.021 | % | |
| Rear Temperature | 169 - 235 | °C | |
| Middle Temperature | 188 - 251 | °C | |
| Front Temperature | 199 - 272 | °C | |
| Nozzle Temperature | 204 - 228 | °C | |
| Processing (Melt) Temp | 203 - 250 | °C | |
| Mold Temperature | 34.4 - 60.6 | °C | |
| Injection Pressure | 84.2 - 155 | MPa | |
| Back Pressure | 0.258 - 44.1 | MPa | |
| Screw Speed | 45 - 47 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PS (HIPS)This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 70.3 | °C | |
| Drying Time | 1.5 | hr | |
| Cylinder Zone 1 Temp. | 180 - 185 | °C | |
| Cylinder Zone 2 Temp. | 193 - 200 | °C | |
| Cylinder Zone 3 Temp. | 199 - 220 | °C | |
| Cylinder Zone 4 Temp. | 208 - 221 | °C | |
| Cylinder Zone 5 Temp. | 212 - 213 | °C | |
| Adapter Temperature | 213 | °C | |
| Melt Temperature | 212 - 225 | °C | |
| Die Temperature | 202 - 216 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PS (HIPS)This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RESPOND™ EX4290 | LyondellBasell Industries | Polyolefin, Unspecified | RESPOND™ |
| NOVAPOL® HE-Y449-AC | NOVA Chemicals | HDPE | NOVAPOL® |
| Hyundai EP PPF HT130 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Lumid® GP3300A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| Plenco 00755 (Injection) | Plastics Engineering Co. | Mel Phenolic | Plenco |