LNP™ LUBRICOMP™ RL004S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FagymG_LNP-LUBRICOMP-RL004S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4040 HS Product reorder name: RL004S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.9 to 3.3 | % | |
| Across Flow : 24 hr | 1.9 to 3.3 | % | |
| Water Absorption (24 hr, 50% RH) | 0.56 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2480 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 63.1 | MPa | ASTM D638 |
| Yield | 55.9 | MPa | ISO 527-2 |
| Break | 63.1 | MPa | ASTM D638 |
| Break | 55.9 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.4 | % | ASTM D638 |
| Yield | 6.7 | % | ISO 527-2 |
| Break | 6.2 | % | ASTM D638 |
| Break | 7.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2280 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 88.0 | MPa | ASTM D790 |
| -- | 84.9 | MPa | ISO 178 |
| Wear Factor - Washer | 16.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.30 | J | ASTM D3763 |
| -- | 0.940 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 65.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 9.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 5 Z | RTP Company | Acetal (POM) Copolymer | RTP |
| Network Polymers PP PPB 25 1010 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Nypol® PA A3 D15 TZ CNZ0311 NR388 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| AMTOPP CI35 | Inteplast Group | PP, Unspecified | AMTOPP |
| Elastollan® 1180A50 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |