Sup-tech P704
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fa5Gss_Sup-tech-P704.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech P704 is a Polypropylene product filled with 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | DIN 53479 |
| Melt Mass-Flow Rate (MFR) | 5.0 to 8.0 | g/10 min | DIN 53735 |
| Molding Shrinkage | 6.0E-3 | % | DIN 53464 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | DIN 53495 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 88 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 44.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 3.0 | % | DIN 53452 |
| Flexural Modulus | 3300 | MPa | DIN 53457 |
| Flexural Stress | 70.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 135 | °C | |
| 1.8 MPa, Unannealed | 120 | °C | |
| Melting Temperature | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Electric Strength | 17 | kV/mm | DIN 53481 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 185 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -M M5001 | TOSOH Corporation | Polyolefin, Unspecified | Melthene® -M |
| SNOLEN® IM 8/51 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Fainplast PVC FKT 0296/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina GRAY PVC COMPOUND -E 813-18/190-Y-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| 3M™ Dyneon™ Fluoroplastic FEP FLEX6305Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |