POTICON AT68B

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	Otsuka Chemical Co., Ltd.
Trademark:	POTICON
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FZome9_POTICONAT68B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs.

Advantages

Microscopic reinforcement

Superior friction sliding and wear reduction

Excellent dimensional accuracy and surface smoothness

Highly recyclable

Applications

Automotive Parts (gears, bearings)

LED Reflectors

Watch Parts (gears, ground plane)

Camera (image stabilization parts)

Sliding Parts (gears, wheel bearing)

Camera Module Parts

Motor Parts (cog-wheels, bearings)

AT68B Property: High strength

General Information
Features	High Dimensional Stability Low friction coefficient High strength Recyclable materials
Uses	LEDs Gear Application in Automobile Field Camera application Bearing
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.83	g/cm³	ASTM D792
Molding Shrinkage
Flow	0.60	%
Transverse flow	1.7	%
Water Absorption (Equilibrium)	0.20	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	90		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	105	MPa	ASTM D638
Tensile Elongation (Break)	2.2	%	ASTM D638
Flexural Modulus	13700	MPa	ASTM D790
Flexural Strength	170	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	32	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	4.1E-5	cm/cm/°C	ASTM D696
Heat Distortion	150	°C	ASTM D648

Injection	Nominal Value	Unit
Processing (Melt) Temp	185 - 215	°C
Mold Temperature	60 - 100	°C
Injection Pressure	70.0 - 100	MPa

Resin Grade	Manufacturer	Category	Trademark
ResMart Ultra PBT 10	ResMart	PBT	ResMart Ultra
TRILOY® 210NH	Samyang Corporation	PC+ABS	TRILOY®
Karina BRONZE PVC COMPOUND 813D11/ 4-IS-AS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LUVOCOM® 1/CF/10/GK/20/TF/5/BK	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®
TECACOMP® PA66 TC white 4039	Ensinger GmbH	Nylon 66	TECACOMP®