Ultrason® E 2010 MR SW 10111
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FZXDU3_Ultrason-E-2010-MR-SW-10111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, medium viscosity standard injection moulding grade, demolding optimized. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.86 | % | |
| Flow | 0.82 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 2.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | % | |
| Viscosity Number 1 | 56.0 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 154 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2650 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.9 | % | ISO 527-2/50 |
| Tensile Creep Modulus 2(1000 hr) | 2700 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Glass Transition Temperature 3 | 225 | °C | ISO 11357-2 |
| CLTE - Flow | |||
| 23 to 80°C | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| 180°C | 5.9E-5 | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature - short cycle operation | 220 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 300 | mm/sec |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.7E-3 | ||
| 1 MHz | 0.014 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 100 | V | |
| Solution B | 100 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 340 | °C | |
| Middle Temperature | 350 | °C | |
| Front Temperature | 360 | °C | |
| Nozzle Temperature | 360 | °C | |
| Processing (Melt) Temp | 340 to 390 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 2 . | strain <= 0.5%, 23°C |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 311-G13 HS | Custom Resins Group | Nylon 66 | Nylene® |
| DOW™ Electrical & Telecommunications DFDA-1648 NT EXP1 | The Dow Chemical Company | TP, Unspecified | DOW™ Electrical & Telecommunications |
| ESPRENE EPDM 501A | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| LNP™ LUBRICOMP™ DBL34 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| Vistalon™ 5702 | ExxonMobil Chemical | EPDM | Vistalon™ |