SLOVALEN® PC 51 C 30
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FYsvd1_SLOVALEN-PC-51-C-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified homopolymer and copolymer PP for injection moulding with the contenct of 30% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C depending on the talc content. Decreased shrinkage. Packing material, garden flower-pots, toys, dowels, clamps, hinge, office chairs, holders, covers of motors, chassis, protection trims in the automotive industry, electroinstallation boxes in the electrical industry. Fulfills the glow wire 750°C. Delivered in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.9 | % | |
| Flow | 1.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 21 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/B |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 82 H 20 | SILON s.ro | PP Homopolymer | TABOREN |
| Multi-Flex® TPO 2503 S | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| BESTNYL SE15VI01A | Triesa Plastics | Nylon 66 | BESTNYL |
| Exelene® PP H0901 | Montachem International, Inc. | PP Homopolymer | Exelene® PP |
| Kazan LLDPE PE2NT05-5 | Kazanorgsintez Joint Stock Company | LLDPE | Kazan LLDPE |