Order Products : sales@su-jiao.com
MAJORIS DE168 - 8689
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FX7twc_MAJORIS-DE168---8689.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DE168 - 8689 is a 15 % mineral filled polypropylene elastomer modified compound intended for injection moulding. DE168 - 8689 has been developed especially for the automotive interior parts, requiring good impact strength/stiffness, very good scratch resistance and UV resistance. The product is available in natural (DE 168) and black (DE 168-8229) but other colours can be provided on request. APPLICATIONS Automotive interior parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| 0°C | 7.0 | kJ/m² | ISO 179/1A |
| 23°C | 30 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC5GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Chiao Fu PA66 MD312G43 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Karina CLEAR PVC COMPOUND 800/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OPNYL OP6GF33 | Ovation Polymers Inc. | Nylon 6 | OPNYL |
| PolyFibra® PF-AHD01 | FuturaMat | ABS | PolyFibra® |