Novalloy-S S4100 (Type V)
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FWiYPS_Novalloy-S-S4100-Type-V-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-S S4100 (Type V) is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific. Primary attribute of Novalloy-S S4100 (Type V): Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 28 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 101 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 0 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 36.0 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 2 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 230 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 26 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-1 | ||
| 1.00 mm | V-0 | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP R7021-50RNA | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Aplax P0050FN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| DURANEX® 7400W | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Kapex C322 | Ginar Technology Co., LTD. | PC | Kapex |
| Rotuba CAP CP801 (10% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |