LUVOCOM® 50-8479/BL-1 Datasheet,PC,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®50-8479/BL-1 is a polycarbonate (PC) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main characteristics of 50-8479/BL-1 are: good dimensional stability. Typical application areas include: engineering/industrial accessories Tools business/office supplies food contact applications Sporting goods

General Information
Features	Good dimensional stability
Uses	Non-specific food applications Engineering accessories Machine/mechanical parts Business equipment Sporting goods Medical/nursing supplies Mold/Mold/Tool
Appearance	Blue

Physical	Nominal Value	Unit	Test Method
Density	1.36	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	16.0	cm³/10min	ISO 1133
Molding Shrinkage	0.50 - 0.80	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.20	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2
Tensile Stress (Break)	55.0	MPa	ISO 527-2
Tensile Strain (Yield)	5.0	%	ISO 527-2
Flexural Modulus	2000	MPa	ISO 178
Flexural Stress	80.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.8	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	150	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	100	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	130	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+12	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0 - 6.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	280 - 300	°C
Middle Temperature	290 - 310	°C
Front Temperature	300 - 320	°C
Nozzle Temperature	290 - 310	°C
Processing (Melt) Temp	295	°C
Mold Temperature	80.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PC , Polycarbonate
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FWLAy4_LUVOCOM-50-8479-BL-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sindustris PP HM2301	Sincerity Australia Pty Ltd.	PP, Unspecified	Sindustris PP
Kumho SAN SAN 330I	Korea Kumho Petrochemical Co., Ltd.	SAN	Kumho SAN
Kuraray Poval® LM-10HD	Kuraray Co., Ltd.	PVOH	Kuraray Poval®
Pebax® Clear 400	Arkema	PEBA-Ether	Pebax®
Sylvin 802-88 CLEAR	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin