LNP™ STAT-KON™ MD000A compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FWDqnO_LNP-STAT-KON-MD000A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MD000A is a compound based on Polypropylene resin containing Carbon. Added features of this grade are: Electrically Conductive, Exceptional Processing. Also known as: LNP* STAT-KON* Compound MD000A Product reorder name: MD000A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1880 | MPa | ASTM D638 |
| -- | 1770 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 26.0 | MPa | ASTM D638 |
| Break | 25.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.1 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 1650 | MPa | ASTM D790 |
| -- 5 | 1670 | MPa | ISO 178 |
| Flexural Stress | 40.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 46 | J/m | ASTM D256 |
| 23°C 6 | 4.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 830 | J/m | ASTM D4812 |
| 23°C 7 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 26.7 | J | ASTM D3763 |
| -- | 8.44 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 90.8 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 56.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 55.9 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purgex™ 459 Plus | Neutrex, Inc. | PE, Unspecified | Purgex™ |
| Michimid K4200GF33-01 | API Polymers, Inc. | Nylon 66 | Michimid |
| Spartech Polycom SC8F-2088 | Spartech Polycom | PPE+PS | Spartech |
| Escorene™ Ultra LD 721.IK | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hylon® N2015THL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |