LNP™ LUBRICOMP™ RAL32 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FVmXzw_LNP-LUBRICOMP-RAL32-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* RAL32 is a compound based on Nylon 66 resin containing 10% Aramid, 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RAL-4032 Product reorder name: RAL32 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.74 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3850 | MPa | ASTM D638 |
| -- | 3860 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 83.0 | MPa | ASTM D638 |
| Break | 78.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 5.9 | % | ASTM D638 |
| Break | 6.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3480 | MPa | ASTM D790 |
| -- 5 | 3480 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 113 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 124 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 123 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.34 | ||
| vs. Itself - Static | 0.30 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.600 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 46 | J/m | ASTM D256 |
| 23°C 8 | 3.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 470 | J/m | ASTM D4812 |
| 23°C 9 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.96 | J | ASTM D3763 |
| -- | 1.42 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 254 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 242 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 115 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Latishield 36/AR-08A G/17-V0E | LATI S.p.A. | ABS | Latishield |
| Daelim Po1y® XP6070 | DAELIM INDUSTRIAL CO., LTD. | mHDPE | Daelim Po1y® |
| LEXAN™ XHT5146 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 9812-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ EXL5689 resin | SABIC Innovative Plastics | PC | LEXAN™ |