Lupoy® 1603-06
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FVe72G_Lupoy-1603-06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOY PC 1603-06 resin is designed for extrusion products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 56.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 90 | % | |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(23°C, 3.20 mm) | 890 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 126 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 2 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 0.25 mm Notch Depth |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE LLD2025 | Trademark Plastics Corporation | LLDPE | Trademark PE |
| TRIEL® 5350 | Samyang Corporation | TPEE | TRIEL® |
| Evermore PUR UP-6042NR | Evermore Chemical Industry Co., Ltd. | PUR-Ester | Evermore PUR |
| Elastron® D D101.A90.N | Elastron USA, Inc. | SBS | Elastron® D |
| Karina IVORY PVC COMPOUND 807D10/96-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |