Solef® 8808/0902
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | A. Schulman Europe |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FUwVCg_Solef-8808-0902.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon fibres reinforced - Injection |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 3.00 | cm³/10min | ISO 1133 |
| 230°C/5.0 kg | 8.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 7250 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 2.5% strain 3 | 80.0 | MPa | ISO 178 |
| 1.8% strain | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 162 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 151 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 171 | °C | ISO 306/A50 |
| -- | 145 | °C | ISO 306/B50 |
| Thermal Conductivity | 0.36 | W/m/K | ISO 22007-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.60 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.20 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 900 | °C | IEC 60695-2-13 |
| 3.00 mm | 900 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break at 2.5% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHM3600 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| TORZEN Marathon™ FRU4800XHL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN Marathon™ |
| Vyncolit® X7012 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Fibremod™ GB601HP | Borealis AG | PP, Unspecified | Fibremod™ |
| SABIC® SUPEER™ 8415 | Saudi Basic Industries Corporation (SABIC) | mLLDPE | SABIC® SUPEER™ |