Next Nylon 66 Industrial Series PX-02BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Industrial Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FTyNbG_Next-Nylon-66-Industrial-Series-PX-02BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 UnFilled Black Compound Product Applications Genral purpose application such as Textile parts, pulley sliding wheel, door handle and screw caps etc Benefits Good dimension stability & Good strength |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.75 | -- | % | |
| Across Flow | 1.3 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.1 | -- | % | |
| Saturation 1 | 6.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 80 | -- | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 75.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | > 30 | % | ASTM D638 |
| Flexural Modulus | 3000 | 2400 | MPa | ASTM D790 |
| Flexural Strength | 110 | 85.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 78 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 180 | -- | °C | |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | |
| Melting Temperature | 260 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 22 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 275 | °C | |
| Front Temperature | 275 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S2 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Sasol Polymers PP ESV200 | Sasol Polymers | PP Random Copolymer | Sasol Polymers PP |
| Sindustris ABS LAF416HT | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sindustris PC GP2103 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| KOPA® KN133G33HIBK | Kolon Plastics, Inc. | Nylon 6 | KOPA® |