AKROTEK® PEEK CF 30 black (5049)
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FTi4VR_AKROTEK-PEEK-CF-30-black-5049-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PEEK CF 30 black (5049) is a 30% carbon fibre reinforced polyetheretherketone with high flexural strength and good sliding properties Applications are mainly elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength and high stiffness in a temperature environment above 150°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.39 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 68.0 | -- | cm | Internal Method |
| Humidity Absorption - 62% RH (70°C) | 0.22 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 1.8 | -- | % | ISO 178 |
| Tensile Modulus | 25500 | 25000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 235 | 228 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 23000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 345 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | 38 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | > 280 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 230 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 342 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® A3 H CF40 | Nilit Plastics | Nylon 66 | NILAMID® |
| 4MID® 9A22115 HR | 4Plas | Nylon 66 | 4MID® |
| Arnite® TZ6 280 | DSM Engineering Plastics | PBT | Arnite® |
| COPYLENE® CR300CL-01 | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Karina IVORY PVC COMPOUND 550D35/ 1-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |