Novodur® H605
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Novodur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FTXw3F_Novodur-H605.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novodur H605 is a high heat injection molding grade with enhanced flowability and reduced emission. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 105 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 2.5 | % | |
| Break, 23°C | > 15 | % | |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 90 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength 1(1.50 mm) | 33 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.0E-3 | ||
| 1 MHz | 8.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec |
| Note Message | |
|---|---|
| 1 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenogel® ABS A3 G20 NTLA010 AB321 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| Nipoflex® 633 | TOSOH Corporation | EVA | Nipoflex® |
| CompaDur® 121 black (018) | DimeLika Plast GmbH | PBT | CompaDur® |
| ELIX™ ABS P3H-AT | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Lionpol TE-70018 | Lion Polymers Incorporated | TPE | Lionpol |