Bio-Flex® F 1110 (prev. Bio-Flex® 221 F) Biodegradable compound for film extrusion Compostable Compound according to EN 13 432, max. layer thickness 110µm Certified according to: DIN Certco Compound registration no.: 7W0087 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Apparent Density | 0.76 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 - 4.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 - 3.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 230 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | > 300 | % | ISO 527-2 |
| Flexural Modulus | 215 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 6.00 | MPa | ISO 178 |
| Tensile Elongation at Break | No Break | ISO 527 | |
| Flexural Strain at Break | No Break | ISO 178 | |
| Tensile fracture strength | No Break | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 68.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | > 155 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.30 | % | |
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Cylinder Zone 4 Temp. | 160 | °C | |
| Adapter Temperature | 165 | °C | |
| Melt Temperature | < 190 | °C | |
| Die Temperature | 165 | °C |
| Extrusion instructions |
|---|
| Water jacket (feed): 35°CDie gap: 0.8 - 1.2 mmDie diameter: up to 400 mmBlow film ratio: 2.5 - 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PGHS35-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| AIE PA66 60G6F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| ADENE NCQAD | A.D. Compound spa | PP Homopolymer | ADENE |
| Electrafil® PVDF C BK | Techmer Engineered Solutions | PVDF | Electrafil® |
| Sylvin 8240-95FU White 1508 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |