Infino TK-2046HM
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FR6HCw_Infino-TK-2046HM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-2046HM is a Polycyclohexylenedimethylene Terephthalate (PCT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Ash Content | |||
| -- | 41 | % | ISO 3451 |
| -- | 41 | % | ASTM D5630 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 61.0 | MPa | ASTM D638 |
| Yield | 620 | MPa | ISO 527-2/5 |
| Break | 67.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 1.5 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 3 | |||
| -- | 7600 | MPa | ASTM D790 |
| -- | 77000 | MPa | ISO 178 |
| Flexural Strength 4 | |||
| -- | 78.0 | MPa | ASTM D790 |
| -- | 800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 2.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 6(23°C) | 13 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 29 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 26 | J/m | ASTM D256 |
| 23°C 7 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 150 | J/m | ASTM D256 |
| 23°C 8 | 16 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 250 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 250 | °C | ISO 75-2/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index (3.20 mm) | 4.0 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 290 to 295 | °C | |
| Middle Temperature | 300 | °C | |
| Front Temperature | 305 to 310 | °C | |
| Nozzle Temperature | 310 | °C | |
| Mold Temperature | 130 to 160 | °C | |
| Injection Pressure | 118 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Thickness: 4 mm |
| 6 . | Thickness 4 mm |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sultron® R40-WH | Asia International Enterprise (Hong Kong) Limited | PPS | Sultron® |
| Grivory® GVX-7 H nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| EPO-TEK® OG178 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Kepital® TS-22H | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| K-Prene HYFLEX HF 25 | Technovinyl Polymers India Ltd. | MPR | K-Prene |