CYCOLAC™ INP562 resin
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FQqYlA_CYCOLACINP562resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 6.4 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 16 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3830 | MPa | ASTM D638 |
| -- | 3950 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 74.0 | MPa | ASTM D638 |
| Yield | 78.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 74.0 | MPa | ASTM D638 |
| Fracture | 78.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/50 |
| Fracture 5 | 2.9 | % | ASTM D638 |
| Fracture | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3780 | MPa | ASTM D790 |
| -- 7 | 3460 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 74.6 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.2 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 23 | J/m | ASTM D256 |
| 23°C | 23 | J/m | ASTM D256 |
| -30°C 9 | 2.4 | kJ/m² | ISO 180/1A |
| 23°C 10 | 2.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 97.6 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 84.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 86.9 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/B50 |
| -- | 106 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-315 (Roto) | Ravago Manufacturing Americas, LLC | HDPE | Ravago Compounds |
| Spartech Polycom SPF7010 | Spartech Polycom | PC | Spartech |
| TEREZ PA 6.6 7500 TF 15 UV | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| WPP JOSB26569-Black | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP |
| LEXAN™ EXL1434T resin | SABIC Innovative Plastics | PC | LEXAN™ |