Starpylen MZ006S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FQgvYB_Starpylen-MZ006S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen MZ006S is a Glass Fiber Reinforced, Polypropylene Injection Molding Resin heat stabilised (also known as Starpylen WT 30GF S3 ) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 5.00 to 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (4.00 mm) | 0.30 to 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 5.0 to 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3000 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 45.0 | MPa | |
| -- 4 | 65.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact Strength 5(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 86.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell HP570U | LyondellBasell Industries | PP Homopolymer | Purell |
| Sylvin 8818-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TPUCO® TPUI-L70 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| FHR Polypropylene 21N2A | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Innoprene 1870N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |