Order Products : sales@su-jiao.com
VALOX™ HX215HP resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FQ1Hon_VALOX-HX215HP-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Flow, Unreinforced, Polybutylene Terephthalate (PBT) with mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. Available in limited colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 80 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 - 2.0 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.34 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2700 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 26.0 | MPa | ASTM D638 |
| Fracture | 49.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.7 | % | ASTM D638 |
| Yield | 3.2 | % | ISO 527-2/50 |
| Fracture 5 | 10 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2260 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 89.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 30 | J/m | ASTM D256 |
| 23°C | 30 | J/m | ASTM D256 |
| -30°C 10 | 2.7 | kJ/m² | ISO 180/1A |
| 23°C 11 | 2.9 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 20.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 150 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 54.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 49.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 180 | °C | ASTM D1525, ISO 306/B120 10 13 |
| -- | 183 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 238 - 254 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 48.9 - 76.7 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.013 - 0.025 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 200 - 230 | °C | |
| Cylinder Zone 2 Temp. | 240 - 255 | °C | |
| Cylinder Zone 3 Temp. | 240 - 275 | °C | |
| Cylinder Zone 4 Temp. | 240 - 275 | °C | |
| Adapter Temperature | 240 - 275 | °C | |
| Melt Temperature | 245 - 260 | °C | |
| Die Temperature | 240 - 275 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsWater Bath Temperature: 25 - 35 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 102186 | RTP Company | PC | RTP |
| ALFATER XL® A80E 1GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| ASTALAC™ ASA 202 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| Asrene® SI 5230 | Chandra Asri Petrochemical | HDPE | Asrene® |
| DAI-EL™ G-802 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |