Braskem PE HB-0454
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FPLMqa_Braskem-PE-HB-0454.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HB0454 is a resin Polyethylene copolymer of High Density of average molecular weight produced for the Unipol® process. The bottle gotten with the HB0454 shows excellent processability, color and superficial appearance, absence of residual odor and good chemical resistance and to the piling up. It presents great easiness to the detachment of barbs being also adjusted for use in rotating machines of high productivity. Application: Small medicine bottles. bottles for cleaning products, cosmetics, food products and tensoative products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.36 | g/10 min | |
| 190°C/21.6 kg | 32 | g/10 min | |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00 mm, 10% Igepal, Compression Molded, F50 | 23.0 | hr | |
| 50°C, 2.00 mm, 100% Igepal, Compression Molded, F50 | 46.0 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 29.0 | MPa | |
| Break, Compression Molded | 31.0 | MPa | |
| Flexural Modulus - 1% Secant (Compression Molded) | 1010 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 69.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sorona® 3030GV NC010 | DuPont Performance Polymers | PTT | Sorona® |
| XYRON™ L654V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NYCOA Polyamide ASN 27 440 KNF | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Kumho ABS H2938L | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| LEXAN™ BM5225X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |