PRL PPX-EN-FR3
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FOachV_PRL-PPX-EN-FR3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-EN-FR3 is a polyphenylene ether PS (PPE PS) product,. It can be processed by extrusion and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 4.0 - 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 64.1 | MPa | ASTM D638 |
| Fracture, 3.18mm | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 25 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| Dart Drop Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 129 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 121 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| 1.70 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 105 | °C | UL 746 |
| 1.70 mm | 105 | °C | UL 746 |
| 3.00 mm | 105 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| 1.70 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) (0.750 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 1 | UL 746 | |
| 1.70 mm | PLC 1 | UL 746 | |
| 3.00 mm | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (0.750 mm) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 1.70 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, BK | V-2 | UL 94 | |
| 1.50 mm, ALL | V-1 | UL 94 | |
| 1.70 mm, ALL | V-1 | UL 94 | |
| 3.00 mm, ALL | V-1 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 204 | °C | |
| Cylinder Zone 2 Temp. | 227 | °C | |
| Cylinder Zone 3 Temp. | 227 | °C | |
| Melt Temperature | 227 - 254 | °C | |
| Die Temperature | 249 | °C |
| Extrusion instructions |
|---|
| Do not exceed 8 hours drying time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AMN D | Arkema | Nylon 12 | Rilsan® |
| Maxelast® P3945C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Anjacom® 050/7020 | Almaak International GmbH | PC+ABS | Anjacom® |
| Cheng Yu E500G10 | Cheng Yu Plastic Company Limited | PC+PET | Cheng Yu |
| Generic Polyolefin, Unspecified - Calcium Carbonate | Generic | Polyolefin, Unspecified | Generic |